鋁板的擠壓過程表面起泡是由什么原因造成的?

來源:http://www.menguosenlin.cn/ 發(fā)布時(shí)間:2020-12-22

在鋁板的擠壓過程中,很容會(huì)出現(xiàn)表面起皮或氣泡,到底是什么原因造成的呢?該用什么方法來消除呢?現(xiàn)在就由鋁板生產(chǎn)廠家為您排異解惑吧!
In the process of aluminum plate extrusion, it is easy to appear surface peeling or bubbles. What is the reason? How to eliminate it? Now let the aluminum plate manufacturer solve the problem for you!
什么是氣泡或起皮:在制品表面出現(xiàn)凸形的泡,常見于頭、尾部,完整的叫氣泡,已破裂的叫起皮。
What is bubble or flaking: convex bubble appears on the surface of the product, common in the head and tail, complete called bubble, has broken called peeling.
一、鋁板擠壓產(chǎn)生氣泡、起皮的原因
1、 Causes of air bubble and peeling during extrusion of aluminum plate
1.擠壓筒、擠壓墊磨損超差,擠壓筒和擠壓墊尺寸配合不當(dāng),使用的墊片直徑差超過允許值;
1. The wear of extrusion cylinder and cushion is out of tolerance, the size of extrusion cylinder and extrusion pad is not matched properly, and the diameter difference of gasket used exceeds the allowable value;
2.擠壓筒和擠壓墊太臟,粘有油污、水分、石墨等;
2. The extrusion cylinder and pad are too dirty, with oil, moisture, graphite, etc;

 


3.潤滑油中含有水;
3. The lubricating oil contains water;
4.鑄錠表面鏟槽太多,過深,或鑄錠表面有氣孔、砂眼,組織疏松、有油污等;
4. There are too many grooves on the surface of the ingot, which are too deep, or there are pores and sand holes on the surface of the ingot, and the structure is loose and greasy;
5.更換合金時(shí),筒內(nèi)未清理干凈;
5. The cylinder is not cleaned when the alloy is replaced;
6.擠壓筒溫度和擠壓鑄錠溫度過高;
6. The temperature of extrusion cylinder and ingot is too high;
7.鑄錠溫度、尺寸超過允許負(fù)偏差;
7. The ingot temperature and size exceed the allowable negative deviation;
8.鑄錠過長,填充太快,鑄錠溫度不均,引起非鼓形填充,因而筒內(nèi)排氣不完全,或操作不當(dāng),未執(zhí)行排氣工序;
8. Too long ingot, too fast filling, uneven ingot temperature, resulting in non drum filling, so that the exhaust in the cylinder is not complete, or improper operation, and the exhaust process is not carried out;
9.??自O(shè)計(jì)不合理,或切殘料不當(dāng),分流孔和導(dǎo)流孔中的殘料被部分帶出,擠壓時(shí)空隙中的氣體進(jìn)入表面。
9. The design of die hole is unreasonable, or the cutting of scrap is improper. The residual material in the diversion hole and diversion hole is partially carried out, and the gas in the space gap enters the surface during extrusion.
二、鋁板擠壓產(chǎn)生氣泡、起皮的消除方法
2、 Elimination of air bubble and peeling during extrusion of aluminum plate
1.合理設(shè)計(jì)擠壓筒和擠壓墊片的配合尺寸,經(jīng)常檢查工具尺寸,保證符合要求,擠壓筒出現(xiàn)大肚要及時(shí)修理,擠壓墊不能超差;
1. Reasonably design the matching size of the extrusion cylinder and the extrusion gasket, check the tool size regularly to ensure that they meet the requirements, repair the big belly of the extrusion cylinder in time, and the extrusion pad shall not exceed the tolerance;
2.工具、鑄錠表面保持清潔、光滑和干燥;
2. Keep the surface of tools and ingots clean, smooth and dry;
3.更換合金時(shí),徹底清筒;
3. Clean the cylinder thoroughly when replacing the alloy;
4.經(jīng)常檢查設(shè)備和儀器,防止溫度過高、速度過快;
4. Check the equipment and instruments frequently to prevent the temperature from being too high and the speed too fast;
5.嚴(yán)格執(zhí)行工藝規(guī)程和各項(xiàng)制度;
5. Strictly implement the process procedures and systems;
6.合理設(shè)計(jì)、制造工模具,導(dǎo)流孔和分流孔設(shè)計(jì)成1°-3°內(nèi)斜度;嚴(yán)格操作,正確剪切殘料和完全排氣。
6. Reasonable design and manufacture of tools and moulds, the diversion hole and the diversion hole should be designed with an internal slope of 1 ° to 3 ° and the operation should be strictly carried out to cut the residual materials correctly and exhaust completely.
通過專家的答疑解惑,相信大家對(duì)鋁板擠壓產(chǎn)生氣泡、起皮的原因及消除方法都有了深刻的了解,在日常生產(chǎn)中避免這些問題,就能減少損耗,提高成品率。
Through the expert's question and answer, I believe everyone has a deep understanding of the causes and elimination methods of bubbles and peeling in aluminum plate extrusion. If we avoid these problems in daily production, we can reduce the loss and improve the yield.

亚洲欧美日韩国产一区二区三区-国产欧美日韩一区二区免费| 91精品国产影片一区二区三区-欧美精品久久久精品一区二区| hd在线观看一区二区-免费一区二区三区毛片在线| 亚洲日本一区二区三区黄色电形-中文字幕乱码免费熟女| 欧美一区二区三区调教视频-三上悠亚国产精品一区二区三区| 欧美日韩国产亚洲免费-肉体粗喘娇吟国产91| 欧美日韩国产综合新一区-国产综合av一区二区三区| 亚洲区欧美区在线视频-亚洲碰碰人人AV熟女天堂| 人妻日韩精品中文字幕图片-麻豆极度性感诱人在线露脸| 日韩中文字幕v亚洲中文字幕-日韩亚洲av免费在线观看| 十九禁止观看无码视频-亚洲国产激情福利专区| 两性污污视频网站在线观看-亚洲欧美日韩激情一区| 青青草原免费国产在线视频-精品人妻乱码一区二区三区四区| 亚洲av专区在线观看国产-丰满人妻av一区二区三区| 日韩亚洲一区二区三区av-欧美综合在线观看一区二区三区| 99久热精品免费观看四虎-亚洲天堂精品视频在线| 91精品国产无线乱码在线-999精品视频免费看| 国模自慰一区二区三区-日韩一级黄色片天天看| 中文字幕日韩不卡久久-五月天中文字幕啊av| 丝袜美腿人妻连续中出-在线观看日韩三级视频| 一区二区三区日本韩国欧美-日本1区2区3区4区在线观看| 中文字幕精品一区二区日本99-青青国产成人久久91网| 亚洲国产精品一区二区av-日本一级黄色一区二区| 人妻日韩精品中文字幕图片-麻豆极度性感诱人在线露脸| 亚洲精品一区网站在线观看-黄页视频免费观看网站| 18禁真人在线无遮挡羞免费-中文字幕精品一区二区三区四区| 蜜臀一区二区三区精品在线-99久久久精品免费看国产| 日韩av电影一区二区网址-老熟妇仑乱视频一区二| 色综合色综合久久综合频道-埃及艳后黄版在线观看| 亚洲中文一二三av网-亚洲天堂成人免费在线| 免费av一区在线观看-国产精品视频高潮流白浆视频免费| 99在线观看精品视频免费-国产极品一区二区三区四区| 亚洲一区精品一区在线观看-日本久久久一区二区三区| 亚洲最新国产无人区123-黄片一区二区在线观看| 亚洲精品激情一区二区-久久成人国产欧美精品一区二区| 亚洲日本一区二区三区黄色电形-中文字幕乱码免费熟女| 蜜臀av日日欢夜夜爽一区-av在线免费永久播放| 在线成色中文综合网站-国产二区精品视频在线观看| 丝袜美腿人妻连续中出-在线观看日韩三级视频| 久久网站中文字幕精品-三级精品久久中文字幕| 亚洲综合久久综合激情-日韩欧美精品人妻二区少妇|